Shrinkage ratio: 2:1
Working temperature: -55℃~200℃
Shrinking temperature: 100℃~175℃
High flame retardant, soft and elastic, oil and solvent resistance,
Environmental standards: RoHS
Executive standard: UL224, VW-1
Standard color: black
product description:
The product is made of modified fluorine rubber, which is soft, flame retardant, high temperature resistant, and resistant to various chemicals and solvents. It is widely used in military vehicles, high-speed trains, ship equipment, and other corrosive military and civilian occasions.
Features:
Shrinkage ratio: 2:1
Working temperature: -55℃~200℃
Shrinking temperature: 100℃~175℃
High flame retardant, soft and elastic, oil and solvent resistance,
Environmental standards: RoHS
Executive standard: UL224, VW-1
Standard color: black
Specification | Supply inner diameter (mm) | Size after fully contracted(mm) | shape | standard packaging (M/plate) | ||
mm | inch | the inside diameter of | Wall thickness | |||
Φ2.4 | 3/32 | ≥3.2 | ≤1.2 | 0.60±0.20 | round | 200 |
Φ3.2 | 1/8 | ≥3.2 | ≤1.6 | 0.65±0.20 | round | 200 |
Φ4.8 | 3/16 | ≥4.8 | ≤2.4 | 0.75±0.20 | round | 100 |
Φ6.4 | 1/4 | ≥6.4 | ≤3.2 | 0.75±0.20 | round | 100 |
Φ9.5 | 3/8 | ≥9.5 | ≤4.8 | 0.75±0.20 | flat | 50 |
Φ12.7 | 1/2 | ≥12.7 | ≤6.4 | 0.75±0.20 | flat | 25 |
Φ19.1 | 3/4 | ≥19.1 | ≤9.5 | 0.90±0.30 | flat | 25 |
Φ25.4 | 1 | ≥25.4 | ≤12.7 | 1.10±0.30 | flat | 25 |
Φ38.11 | 1-1/2 | ≥38.1 | ≤19.1 | 1.30±0.30 | flat | 25 |
Φ50.8 | 2 | ≥50.8 | ≤25.4 | 1.50±0.30 | flat | 15 |
Project | Test Methods | Typical data |
Tensile Strength | ASTM D 2671 | ≥9MPa |
Elongation at break | ASTM D 2671 | ≥350% |
Strength after heat aging | 250°C,168 hours | ≥8MPa |
Elongation at break after heat aging | ≥200% | |
Thermal shock | 300°C,4 hours | No cracks, no drips |
Flame retardant | ASTM D 2671 | Self-extinguishing within 15 seconds |
Electric breakdown strength | ASTM D 2671 | ≥8Kv/mm |
Volume resistivity | ASTM D 876 | ≥10^10Ω.cm |